Malaysia China Foundry Filter can effectively remove various micro-scale inclusions in aluminum melt. The molten aluminum forms a stable laminar flow, which is conducive to filling. The ceramic foam filter has a unique three-dimensional structure, good mechanical strength and chemical stability, and excellent aluminum corrosion resistance. Strictly control the pore size and through-hole rate to obtain a stable filtering effect. There are sealing ceramic fiber gaskets around the Aluminum Furnace Filter to help seal the ceramic filter plate in the filter box.

The filtration efficiency of Malaysia China Foundry Filter is closely related to its correct installation and use. At the same time, due to the filtering process, conventional and necessary measures have been taken in smelting, furnace treatment and casting operations to reduce the appearance of inclusions. It is also necessary to prevent re-contamination of the filtered molten aluminum.

Malaysia China Foundry Filter

How to Install the Porous Ceramic Foam Filters

1. Correctly choose porous ceramic filter:
The selection of filter plate size and hole number specifications must consider factors, such as the flow range of the specific casting type, the maximum level of metal during the filtration process, the total filtration volume and the cleanliness of the original aluminum liquid.

2. The pretreatment of melt filtration cannot be ignored:
For example, conventional slag cleaning and furnace refining in aluminum melting furnaces and holding furnaces. In particular, the online degassing device is still necessary, because it can not only reduce the hydrogen content in the melt, but also remove some non-metallic inclusions.

3. The filter plate must fit the square refractory filter box:
The adaptation of the two makes it easy to seal, which not only prevents metal from flowing into the casting box from the gap without being filtered, but also prevents the foam filter plate from being too light and floating in the aluminum water to cause failure.

4. Need to warm up before use:
Preheat to remove moisture and facilitate preliminary filtration. Electric heating or gas heating can be used for preheating. Normally, it takes about 15 minutes.

5. In the normal filtering process, there is no need to discharge the slag to avoid the knocking and vibration of the filter plate. At the same time, the launder should be filled with molten aluminum to avoid excessive interference with molten aluminum.

6. After casting, put the metal into the launder and filter plate. A vibrator was placed on the filter plate and vibrated for one minute. It can shake off about 75% of the remaining liquid metal from the filter plate.

7. Finally clean up for four weeks, and remove the filter plate after curing.