Metal Filtration

30 10月 Metal Filtration

Metal Filtration

The ceramic filter for aluminium Metal Filtration was prepared by an organic foam impregnation process, and the effect of sintering temperature on the performance of the alumina-based ceramic foam filter.
With the increase of sintering temperature, the compressive strength and thermal shock resistance of alumina-based ceramic foam filter show a trend of increasing first and then decreasing.
When the sintering temperature is 1430 ° C, the two properties are higher.
At this time, due to the uniform grain size, less pore and glass phase content in the ceramic, and the phase containing more mullite phase and less cristobalite phase, the overall performance is best.
At this time, the bulk density of the ceramic was 0.5 g/cm3, the compressive strength was 2.7 MPa, and the number of thermal cycles at 1100 °C-room temperature was 27 times.

Alumina Ceramic Foam Filter, pls contact sales@adtechamm.com

Related posts:

Production of Ceramic Foam Filter for Molten Metal Filtration Aluminum Casting-Molten Metal Filtration Ceramic foam filter molten metal filtration High Temperature Metal Aluminium Filtration Casting Filter Filtration of molten metal using ceramic filters Professional Foundry Foam Filter Ceramic Honeycomb Filter For Metal Filtration Casting Ceramic Foam Filter Alumina Ceramic Filtration Alumina Ceramic Filtration Aluminium and filtration Wetting behavior with Al2O3 and SiC ceramic foam filters Ceramic Foam Filter Manufacturers Reticulated ceramic foam filters Metal Transfer Runner System